In order to make the injection mold process manufacturing show exquisite workpieces, we will heat the injection molds, which not only can improve the precision of the injection molds, but also improve the quality and precision of the workpieces. For everyone to share: Note on the heating process of the injection mold, mainly divided into four parts, namely forging process, preparatory heat treatment, quenching and tempering, stress relief annealing. Here are the points of attention for each link.
First, the forging process. This is an important part of the manufacturing process of injection mold parts. For injection molds of high-alloy tool steels, technical requirements are often imposed on metallographic structures such as material carbide distribution. In addition, the forging temperature range should be strictly controlled, the correct heating specification should be established, the correct forging force method should be used, and the post-forging slow cooling or timely annealing should be carried out.
Second, the preparatory heat treatment. Pre-heat treatment processes such as annealing, normalizing or quenching and tempering should be used depending on the materials and requirements of the working parts of the injection mold to improve the structure, eliminate the structural defects of the forged blank, and improve the processing technology. The high-carbon alloy mold steel can eliminate the reticulated secondary cementite or chain carbide after proper preliminary heat treatment, so that the carbide is spheroidized and refined, and the uniformity of carbide distribution is promoted. This is beneficial to ensure the quality of quenching and tempering and improve the life of the mold.
Third, quenching and tempering. This is the key link in the heat treatment of the mold. If the superheat occurs during quenching and heating, not only will the workpiece cause greater brittleness, but also cause deformation and cracking during cooling, which seriously affects the life of the mold. Special care should be taken to prevent oxidation and decarburization during die quenching. The heat treatment process specification should be strictly controlled. Vacuum vacuum heat treatment can be used if conditions permit. After quenching, it should be tempered in time, and different tempering processes should be adopted according to technical requirements.
Fourth, stress relief annealing. After the injection mold is processed, the stress relief annealing treatment should be carried out. The purpose is to eliminate the internal stress caused by rough machining, so as to avoid excessive deformation and cracking caused by quenching. For molds with high precision requirements, it needs to be subjected to stress relief and tempering after grinding or electric machining, which is beneficial to stabilize mold precision and improve service life.
Heat treatment is the process that every injection mold must go through before leaving the factory. However, not every injection mold factory can be implemented in a standard way. This also requires process technology. The mold factory has set a new standard for mold heating for the industry. Each set of molds produced reaches a precise height.
- Four Key Points Affecting The Quality Of Inject...
- How Do We Deal With The Deformation Of Plastic ...
- How To Improve Mold Quality
- Injection Mold Maintenance
- Factors Affecting The Service Life Of Injection...
- What Are The Plastic Molds When Processing?
- Analysis Of Processing Characteristics Of Plast...
- How To Deal With Plastic Mold Deformation
- How To Reduce Shrinkage Of Plastic Mold
- How Can Plastic Moulds Be Better Done?